Antimony trisulfide
- 2 min read
- 2 chapters
Related on Lably
Through Match and Semiconductor
Antimony trisulfide was also used as the image sensitive photoconductor in vidicon camera tubes. It is a semiconductor with a direct band gap of 1.8–2.5 eV. With suitable doping, p and n type materials can be produced.
Preparation and reactions
Sb2S3 can be prepared from the elements at temperature 500–900 °C:
- 2 Sb + 3 S → Sb2S3
Sb2S3 is precipitated when H2S is passed through an acidified solution of Sb(III). This reaction has been used as a gravimetric method for determining antimony, bubbling H2S through a solution of Sb(III) compound in hot HCl deposits an orange form of Sb2S3 which turns black under the reaction conditions.
Sb2S3 is readily oxidised, reacting vigorously with oxidising agents. It burns in air with a blue flame. It reacts with incandescence with cadmium, magnesium and zinc chlorates. Mixtures of Sb2S3 and chlorates may explode.
In the extraction of antimony from antimony ores the alkaline sulfide process is employed where Sb2S3 reacts to form thioantimonate(III) salts (also called thioantimonite):
- 3 Na2S + Sb2S3 → 2 Na3SbS3
A number of salts containing different thioantimonate(III) ions can be prepared from Sb2S3. These include:
- [SbS3]3−, [SbS2]−, [Sb2S5]4−, [Sb4S9]6−, [Sb4S7]2− and [Sb8S17]10−
Schlippe's salt, Na3SbS4·9H2O, a thioantimonate(V) salt is formed when Sb2S3 is boiled with sulfur and sodium hydroxide. The reaction can be represented as:
- Sb2S3 + 3 S2− + 2 S → 2 [SbS4]3−
Sign in to keep reading
One more chapter is free with a Lably account.
Structure
The structure of the black needle-like form of Sb2S3, stibnite, consists of linked ribbons in which antimony atoms are in two different coordination environments, trigonal pyramidal and square pyramidal. Similar ribbons occur in Bi2S3 and Sb2Se3. The red form, metastibnite, is amorphous. Recent work suggests that there are a number of closely related temperature dependent structures of stibnite which have been termed stibnite (I) the high temperature form, identified previously, stibnite (II) and stibnite (III). Other paper shows that the actual coordination polyhedra of antimony are in fact SbS7, with (3+4) coordination at the M1 site and (5+2) at the M2 site. These coordinations consider the presence of secondary bonds. Some of the secondary bonds impart cohesion and are connected with packing.